Chlorinated Polyethylene, Cpe, High Density Polyethylene manufacturer / supplier in China, offering CPE, Chlorinated Polyethylene, Thermalplastic Material, Rubber Additives for Reinforcing Agent, Sodium Hexametaphosphate (SHMP), Used in Oil Field, Paper-Making, Textile, Dyeing, Petrochemical Industry, Tanning Industry, Metallurgical Industry and Building, 99.5% Min Aluminium Hydroxide, High Whitness Filler Use, Flame Retardant and so on.

(/ )

Supplier Homepage Product Plastic Material CPE, Chlorinated Polyethylene, Thermalplastic Material, Rubber Additives for Reinforcing Agent

CPE, Chlorinated Polyethylene, Thermalplastic Material, Rubber Additives for Reinforcing Agent

FOB Price: US $1,200 / Ton
Min. Order: 5 Tons
Min. Order FOB Price
5 Tons US $1,200/ Ton
Get Latest Price
Production Capacity: 3000tons/ Month
Transport Package: Plastic Bag N. W. 25/50/1000kg
Payment Terms: L/C, T/T, Money Gram, Western Union

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: CPE135, CM135, CPE230, CM140
  • Usage: General Plastics
  • CAS No.: 6321-66-3
  • Trademark: LY
  • Origin: Shandong
  • Material: Polyethylene/PE
  • Color: White
  • Purity: 99%
  • Specification: SGS ISO
  • HS Code: 3901909
Product Description
Our advantage:
1. Factory price,
2. Good Quality,
3. Free sample,
4. ISO Cerficate,
5. A long stable supplier,
6. Good support to you

``````````````````````````````````````````````````````````````````````````````````````````````````````````
Specifications
Bargain price
Good flame resistance
Mechanical strength
Electrical properties
Solvent resistance


2: Chemical property:

At room temperature, the performance is very stable, long-term storage at room temperature. Functional group of TAIC is divided into three allyl, general feature with aliphatic olefins, such as a variety of addition reaction, homopolymerization and copolymerization reaction, Prins reaction and so on. Initiated by peroxide, TAIC occurred more easier for acting than other allylic polymerization, in the air heated to 140° Cthat occurred since the polymerization reaction, become transparent homopolymer, hard.

3: Toxicity:

Mice ( take orally ) LD59=666mg/kg (nearly non-toxic ). Homopolymer and vinyl monomer of TAIC and TAIC crosslinked thermoplastic into non-toxic products.


4: Application

1), Used for a variety of thermoplastic plastics ( polyethylene, polyvinyl chloride, chlorinated polyethylene, polystyrene, EVA ) crosslinking and modification. Thermal cross-linking generally add volume 1-3%, and the volume two cumene oxidation ( DCP ) is 0.2-1%; Adding amount of radiation crosslinking is within 0.5-2%, no need to add DCP. After cross-linking the heat resistance, flame resistance, solvent resistance, mechanical strength and electrical properties of the products can be improved significantly, . It greatly enhances the quality of the products than simply use peroxide crosslinking system, what's more, it is without peculiar smell. Typical for polyethylene, polyethylene / chlorinated polyethylene, polyethylene and polyethylene /EVA XLPE cable of high, low foaming products.

2 )The help of special rubber vulcanization of ethylene-propylene rubber, fluorine rubber, CPE r ( CPE, and DCP general dosage is 0.5-4% ), can significantly shorten the curing time, increase the strength, wear resistance, solvent resistance and corrosion resistance.

3) Acrylic acid, styrene-type ion-exchange resin is crosslinked...It can be used less amount than Divinylbenzene crosslinker of crosslinking agent however it is easier to get high quality, excellent preparation stain resistant, high strength, large aperture, heat resistance, acid and alkali resistance, oxidation resistance of ion exchange resin. That makes it as a recent development, ion exchange resin which has excellent prospects.

4. The modified polyacrylate, poly alkyl acrylate. Improving the heat resistance, optical properties and processing properties significantly. Typical for ordinary organic glass heat-resistant modification.

5. Epoxy, DAP (poly diallyl phthalate) resin modifier which can improve the heat resistance, adhesion, mechanical strength and dimensional stability. It is typically used for epoxy potting compound and modified encapsulation materials.

6. Unsaturated polyester resin and thermoplastic polyester crosslinking and modification. It can significantly improve the heat resistance, chemical resistance, dimensional stability, weather resistance and mechanical properties. It is typically used to improve the heat resistance of hot-pressed unsaturated polyester glass steel products. The usage temperature of the modified products can reach180 ° C

7, TAIC homopolymer -- Poly triallyl cyanurate is a transparent, hard, heat-resistant, electrically insulating excellent resin. It can also be used for bonding such as glass and ceramics. Typical used for the manufacture of laminated safety glass.

8. The internal plasticization, styrene and TAIC copolymerization modification, Transparent, resistance to fragmentation products can be made.
Index
 
Unit
 
Type
 
CPE135
 
CM135
 
CPE230
 
CM140
 
Chlorine content
 
%
 
3337
 
3337
 
2832
 
3842
 
Heat of melting
 
J/g,≤
 
2.0
 
2.0
 
5.0
 
2.0
 
Volatile content
 
%,≤
 
0.4
 
0.4
 
0.40
 
0.40
 
Screenings(0.9mm)
 
%,≤
 
2.0
 
 
 
2.0
 
 
 
Chromoplastid
 
/100g,≤
 
60
 
 
 
60
 
 
 
Shao's hardness
 
A,≤
 
65
 
60
 
70
 
70
 
Tensile strength
 
MPa,≥
 
6.0
 
6.0
 
6.0
 
6.0
 
Mooney viscosity ML(1+4),121
 
MV,≤
 
 
 
80
 
 
 
110
 
 
Send your message to this supplier
Avatar
Miss Jessie
Sales Manager
*From:
To: Miss Jessie
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category